Properties before hardening
Main agent A curing agent B
Color: Colorless transparent Colorless transparent
Specific weight: 1.05 0.96
Viscosity 25℃: 1000-2000CPS 300MAX
2. Conditions of use
1) Mixing ratio: A: B= 100:25 (weight ratio)
2) Hardening conditions: 25℃×10H-12H or 50℃×4H (100g)
3) Usable time: 25℃×60min (100g)
3. Use method
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. Properties after hardening
1) Hardness: shore D < 82
2) Resistance voltage: KV/mm 22
3) Bending strength: Kg/mm2 23
4) Volume resistance: Ohm3 1x1015
5) Surface resistance: Ohmm2 5X1015
6) Thermal conductivity: W/ M.K0.61
7) Induced loss: 1KHZ 0.42
8) High heat resistance temperature: ℃ 80
9) Water absorption: % < 0.15
10) Compressive strength: Kg/mm2 13.4
Specific Uses For Product Craft
Material Epoxy Resin Compatible Material ：
✔Porcelain,
✔Wood,
✔Aluminum,
✔Fiberglass,
✔Glass,
✔Ceramic,
✔Plastic,
✔Carbon Fiber,
✔Concrete,
✔Metal,
✔Stone,
✔AcrylicPorcelain,
✔Wood,
✔Aluminum,
✔Fiberglass,
✔Glass,
✔Ceramic,
✔Plastic,
✔Carbon Fiber,
✔Concrete,
✔Metal,
✔Stone,
✔Acrylic
The above performance data are typical data measured in a laboratory environment with a temperature of 25 ° C and a humidity of 70%, and are for customer reference only.