Epoxy resin adhesive cured at room temperature and low temperature conditions, good leveling, natural defoaming, large area without corrugation, high hardness, room temperature or heating can be cured. It is used in areas with high mechanical performance requirements, such as requiring strong wear resistance and certain impact resistance in machinery factories, hardware factories, wharves, driveways, garages, industrial plants, auto and aircraft repair plants, etc. Cement or terrazzo ground, 3D floor, paper box surface drip glue, large area surface drip glue, Label, card, lighting, lamp strip filling and mold filling, as well as other electronic parts insulation, moisture-proof filling, security cover, etc.
A、Exterior paint
1. Properties before hardening
Main agent A curing agent B
Color: Colorless transparent
Specific weight: 1.15 0.96
Viscosity 25℃: 800-1500CPS 50-300CPS
2. Conditions of use
1) Mixing ratio: A: B= 100:33 (weight ratio)
2) Hardening conditions: 25℃×10H-12H or 50℃×2H (100g)
3) Usable time: 25℃×20min (20kg)
Third, use method
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. Properties after hardening
1) Hardness: shore D < 85
2) Wear resistance 750g/500r g < 0.03
3) Adhesion: (cutting method) grade
B、Middle paint
1. Properties before hardening
Lacquer main agent lacquer curing agent
Color: Colorless transparent light yellow liquid
Specific weight: 1.12 0.94
Viscosity 25℃: 1000-2000CPS 150MAXCPS
2. Conditions of use
1) Mixing ratio: A: B= 100:33 (weight ratio)
2) Hardening conditions: surface dry: 4H-6H hard work; 12H-16H
3) Usable time: 25℃×30min (100g)
Third, use method
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. The lid of the barrel must be sealed after use to avoid product reporting due to moisture absorption.
4. Properties after hardening
1) Hardness: shore D < 80
2) Resistance voltage: KV/mm 22
3) Bending strength: Kg/mm2 28
4) Volume resistance: Ohm3 1x10*15
5) Surface resistance: Ohmm2 5X10*15
6) Thermal conductivity: W/M.K 1.36
7) Induced loss: 1KHZ 0.42
8) Thermal deformation temperature: ℃ 80
9) Water absorption: % < 0.15
10) Compressive strength: Kg/mm2 8.4
C、Bottom paint
1. Properties before hardening
Primer primer curing agent
Color: Colorless transparent colorless transparent or light yellow liquid
Specific weight: 1.14 0.98
Viscosity 25℃: 1200-2000CPS 250MAXCPS
2. Conditions of use
1) Mixing ratio: A: B= 100:50 (weight ratio)
2) Hardening conditions: surface dry: 3H-5H hard work; 10H-14H
3) Usable time: 25℃×30min (100g)
Third, use method
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. The lid of the barrel must be sealed after use to avoid product reporting due to moisture absorption.
4. Properties after hardening
1) Hardness: shore D < 75
2) Resistance voltage: KV/mm 22
3) Bending strength: Kg/mm2 28
4) Volume resistance: Ohm3 1x10*15
5) Surface resistance: Ohmm2 5X10*15
6) Thermal conductivity: W/M.K 1.36
7) Induced loss: 1KHZ 0.42
8) Thermal deformation temperature: ℃ 80
9) Water absorption: % < 0.15
10) Compressive strength: Kg/mm2 8.4
D、3D special paint
1. Properties before hardening
Main agent A curing agent B
Color: Colorless transparent Colorless transparent
Specific weight: 1.15 0.96
Viscosity 25℃: 800-1500CPS 100MAX
2. Conditions of use
1) Mixing ratio: A: B= 100:33 (weight ratio)
2) Hardening conditions: 25℃×8H-10H or 55℃×1.5H (2g)
3) Usable time: 25℃×40min (100g)
3. Methods of use
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. Properties after hardening
1) Hardness: shore D < 85
2) Resistance voltage: KV/mm 22
3) Bending strength: Kg/mm2 23
4) Volume resistance: Ohm3 1x1015
5) Surface resistance: Ohmm2 5X1015
6) Thermal conductivity: W/ M.K0.61
7) Induced loss: 1KHZ 0.42
8) High heat resistance temperature: ℃ 80
9) Water absorption: % < 0.15
10) Compressive strength: Kg/mm2 13.4
The above performance data are typical data measured in a laboratory environment with a temperature of 25 ° C and a humidity of 70%, and are for customer reference only.