Properties before hardening
Main agent A curing agent B
Color: Colorless transparent Colorless transparent
Specific weight: 1.15 0.96
Viscosity 25℃: 1000-2000CPS 100MAXCPS
2. Conditions of use
1) Mixing ratio: A: B= 100:33 (weight ratio)
2) Hardening condition: 25℃×8H-10H(100) 55℃×2H (2g)
3) Usable time: 25℃×40min (100g)
3. Methods of use
1. Working environment: Please keep the container clean,A, B components strictly according to the weight ratio, accurate weighing, along the inner wall of the container fully stir evenly and stand for 3-5 minutes before use.
2. Adjust the amount of glue according to the operating time and dosage to avoid waste. When the temperature is below 15 ° C, please preheat glue A to 30 ° C before adjusting glue, easy to operate (glue A will thicken when the temperature is low); The lid of the barrel must be sealed after use to avoid product scrap due to moisture absorption.
3. When the relative humidity is greater than 85%, the surface of the cured material is easy to absorb the water in the air, forming a layer of white fog, so when the relative humidity is greater than 85%, it is not suitable for normal temperature curing, and it is recommended to use temperature curing.
4. The lid of the barrel must be sealed after use to avoid product reporting due to moisture absorption.
4. Properties after hardening
1) Hardness: shore D < 83
2) Resistance voltage: KV/mm 22
3) Bending strength: Kg/mm2 28
4) Volume resistance: Ohm3 1x10*15
5) Surface resistance: Ohmm2 5X10*15
6) Thermal conductivity: W/M.K 1.36
7) Induced loss: 1KHZ 0.42
8) Thermal deformation temperature: ℃ 80
9) Water absorption: % < 0.15
10) Compressive strength: Kg/mm2 8.4
Specific Uses For Product Craft
Material Epoxy Resin Compatible Material ：
✔Porcelain,
✔Wood,
✔Aluminum,
✔Fiberglass,
✔Glass,
✔Ceramic,
✔Plastic,
✔Carbon Fiber,
✔Concrete,
✔Metal,
✔Stone,
✔AcrylicPorcelain,
✔Wood,
✔Aluminum,
✔Fiberglass,
✔Glass,
✔Ceramic,
✔Plastic,
✔Carbon Fiber,
✔Concrete,
✔Metal,
✔Stone,
✔Acrylic
The above performance data are typical data measured in a laboratory environment with a temperature of 25 ° C and a humidity of 70%, and are for customer reference only.